Welded steel pipes for water and gas pipelines Pipes steel water and gas

INTERSTATE STANDARD

STEEL PIPES
WATER AND GAS

TECHNICAL CONDITIONS

Introduction date 01.01.77

This standard applies to non-galvanized and galvanized steel welded pipes with threaded or knurled cylindrical threads and without threads used for water and gas pipelines, heating systems, as well as for parts of water and gas pipeline structures.

1. ASSORTMENT

1.1. Pipes are made according to the dimensions and weight given in table. one.

At the request of the consumer, light series pipes intended for thread rolling are manufactured according to the dimensions and weight given in Table. 2.

1.2. The length of the pipe is made from 4 to 12 m:

a) measured or multiple measured length with an allowance for each cut of 5 mm and a maximum deviation for the entire length plus 10 mm;

b) unmeasured length.

By agreement between the manufacturer and the consumer, up to 5% of pipes with a length of 1.5 to 4 m are allowed in a batch of off-gauge pipes.

Table 1

Conditional pass	Outside diameter	Pipe Wall Thickness			Weight of 1 m of pipes, kg
Conditional pass	Outside diameter		ordinary	enhanced		ordinary	enhanced

table 2

Conditional pass	Outside diameter	Wall thickness	Weight of 1 m of pipes, kg








Notes: 1. For a thread made by knurling, a reduction in its inner diameter of up to 10% along the entire length of the thread is allowed on the pipe. 2. The mass of 1 m of pipes was calculated with a steel density of 7.85 g / cm 3. Galvanized pipes are 3% heavier than non-galvanized ones.

1.3. Limit deviations in pipe dimensions should not exceed those indicated in Table. 3.

Table 3

Pipe dimensions		Pipe dimensions	Limit deviations for manufacturing precision pipes
Pipe dimensions	elevated	Pipe dimensions		elevated
		Outer diameter with nominal bore:
		over 40 mm
up to 40 mm incl.		Wall thickness
Notes: 1. The maximum deviation in the plus side along the wall thickness is limited by the maximum deviations in the mass of pipes. 2. Pipes of ordinary manufacturing accuracy are used for water pipes, gas pipelines and heating systems. Pipes of increased manufacturing accuracy are used for parts of water and gas pipeline structures.

1.4. Maximum deviations in the mass of pipes should not exceed +8%.

At the request of the consumer, the maximum deviations in mass should not exceed:

7.5% - for the party;

10% - for a single pipe.

(Changed edition, Rev. No. 2, 5).

1.5. The curvature of pipes per 1 m of length should not exceed:

2 mm - with nominal bore up to 20 mm inclusive;

1.5 mm - with nominal bore over 20 mm.

1.6. Pipe threads can be long or short. Thread requirements must comply with those specified in table. 4.

Table 4

Conditional passage, mm	Thread length before run		Conditional passage, mm	Number of threads with conditional passage	Thread length before run
Conditional passage, mm		short	Conditional passage, mm	Number of threads with conditional passage		short

1.7. Pipes with a nominal bore of 6, 8, 10, 15 and 20 mm are wound into coils at the request of the consumer.

Legend Examples

Ordinary pipe, non-galvanized, of the usual manufacturing accuracy, random length, with a nominal bore of 20 mm, a wall thickness of 2.8 mm, without thread and without a coupling:

The same with the clutch:

The same, measured length, threaded:

The same, zinc coated, random length, threaded:

The same, with zinc coating, measured length, with thread:

For pipes for thread rolling, the letter H is indicated after the word "pipe" in the symbol.

For pipes with a long thread, the letter D is indicated after the word "pipe" in the symbol.

For pipes of increased manufacturing accuracy, the letter P is indicated in the symbol after the nominal bore size.

(Revised edition, Rev. No. 1).

2. TECHNICAL REQUIREMENTS

2.1. Pipes are manufactured in accordance with the requirements of this standard and according to the technological regulations approved in the prescribed manner, from steels according to GOST 380 and GOST 1050 without standardization of mechanical properties and chemical composition.

Pipes for parts of water and gas pipeline structures are made of steel according to GOST 1050.

2.2. At the request of the consumer, the ends of pipes to be welded, with a wall thickness of 5 mm or more, must be chamfered at an angle of 35 - 40 ° to the end of the pipe. In this case, an end ring with a width of 1 - 3 mm should be left.

At the request of the consumer, on ordinary and reinforced pipes with a nominal bore of more than 10 mm, the thread is applied to both ends of the pipe.

2.1; 2.2.

2.3. At the request of the consumer, the pipes are equipped with couplings made in accordance with GOST 8944, GOST 8954, GOST 8965 and GOST 8966 at the rate of one coupling for each pipe.

(Revised edition, Rev. No. 3).

2.4. Cracks, captivity, swelling and sunsets are not allowed on the surface of the pipes.

At the ends of the pipes, delamination is not allowed.

Separate dents, ripples, risks, traces of stripping and other defects due to the production method are allowed, if they do not take the wall thickness beyond the minimum dimensions, as well as a scale layer that does not interfere with inspection.

On pipes made by furnace welding, it is allowed to reduce the outer diameter to 0.5 mm at the weld site if there is a gentle thickening of the inner diameter of not more than 1.0 mm in this place.

(Changed edition, Rev. No. 3, 4).

2.5. At the request of the consumer, on pipes with a nominal bore of 20 mm or more, on the inner surface of the pipe seam, the burr must be cut or flattened, while the height of the burr or its traces should not exceed 0.5 mm.

At the request of the consumer, on pipes with a nominal bore of more than 15 mm, made by the method of furnace welding and the method of hot reduction, a gentle thickening of a height of not more than 0.5 mm is allowed on the inner surface of the pipes in the weld zone.

(Changed edition, Rev. No. 2, 3, 4, 5, 6).

2.6. Pipe ends must be cut square. The value of the bevel of the end is allowed no more than 2 °. Burr residues should not exceed 0.5 mm. When removing burrs, the formation of blunting (rounding) of the ends is allowed. It is allowed to cut pipes in the mill line.

By agreement between the manufacturer and the consumer, burrs up to 1 mm are allowed on pipes with a nominal bore of 6–25 mm, made by furnace welding.

(Changed edition, Rev. No. 4, 6).

2.7. Galvanized pipes must have a continuous zinc coating over the entire surface with a thickness of at least 30 microns. The absence of zinc coating on the ends and threads of pipes is allowed.

On the surface of galvanized pipes, blistering and foreign inclusions (hardzinc, oxides, sintered charge), peeling of the coating from the base metal are not allowed.

Separate flux spots and traces of pipes being caught by lifting devices, roughness and slight local zinc deposits are allowed.

It is allowed to correct individual non-galvanized sections by 0.5% of the outer surface of the pipe in accordance with GOST 9.307.

(Changed edition, Rev. No. 3, 4).

2.8. Pipes must withstand hydraulic pressure:

2.4 MPa (25 kgf / cm 2) - pipes, ordinary and light;

3.1 MPa (32 kgf / cm 2) - reinforced pipes.

At the request of the consumer, the pipes must withstand a hydraulic pressure of 4.9 MPa (50 kgf / cm 2)

(Changed edition, Rev. No. 2, 3, 5).

2.9. Pipes with a nominal bore up to 40 mm inclusive must withstand a bend test around a mandrel with a radius equal to 2.5 of the outer diameter, and with a nominal bore of 50 mm - on a mandrel with a radius equal to 3.5 of the outer diameter.

At the request of the consumer, the pipes must withstand the expansion test:

for pipes with nominal bore from 15 to 50 mm - not less than 7%;

for pipes with a nominal bore of 65 or more - at least 4%.

At the request of the consumer, the pipes must withstand the flattening test up to a distance between the flattened surfaces equal to 2/3 of the outer diameter of the pipes.

(Changed edition, Rev. No. 2, 3, 5).

2.10. At the request of the consumer, the mechanical properties of pipes for parts of water and gas pipeline structures must comply with GOST 1050.

2.11. The pipe thread must be clean, without flaws and burrs, and comply with GOST 6357, accuracy class B.

Pipes with cylindrical threads are used when assembling with seals.

2.10; 2.11. (Changed edition, Rev. No. 3, 4).

2.12. In the place of the seam, blackness on the threads of the thread is allowed if the decrease in the normal height of the thread profile does not exceed 15%, and at the request of the consumer does not exceed 10%.

Threads with broken (for cut) or incomplete (for knurled) threads are allowed on threads, provided that their total length does not exceed 10% of the required thread length, and at the request of the consumer does not exceed 5%.

(Changed edition, Rev. No. 2, 3, 5).

2.13. It is allowed on the thread to reduce the useful length of the thread (without run-off) up to 15% compared to that indicated in Table. 4, and at the request of the consumer up to 10%.

(Changed edition, Rev. No. 2, 3, 5).

2.14. Threading on galvanized pipes is carried out after galvanizing.

2.15. (Deleted, Rev. No. 3).

2.16. At the request of the consumer, welded seams of pipes are subjected to control by non-destructive methods.

(Revised edition, Rev. No. 5).

3. ACCEPTANCE RULES

3.1. Pipes are accepted in batches. The batch must consist of pipes of the same size, the same brand and be accompanied by one quality document in accordance with GOST 10692 with an addition for pipes intended for the manufacture of parts for water and gas pipeline structures, made of steel in accordance with GOST 1050: chemical composition and mechanical properties of steel in accordance with document on the quality of the manufacturer of the workpiece.

The mass of the party is not more than 60 tons.

(Changed edition, Rev. No. 3, 4).

3.2. The surface, dimensions and curvature are checked for each pipe of the batch.

It is allowed to apply statistical control methods according to GOST 18242 * with a normal level. Control plans are established by agreement between the manufacturer and the consumer.

* On the territory of the Russian Federation, GOST R 50779.71-99 applies.

The control of the outer diameter of the pipes is carried out at a distance of at least 15 mm from the end of the pipe.

(Changed edition, Rev. No. 3, 4, 5).

3.3. To control the parameters of the thread, to test for expansion, flattening, bending, the height of the internal burr, burr residues, right angle and chamfer angle (for pipes with beveled edges), mechanical properties, no more than 1%, but not less than two pipes from the lot are selected, and for pipes manufactured by continuous furnace welding, two pipes per batch.

(Changed edition, Rev. No. 3, 4).

3.4. All pipes are subjected to weight control.

(Revised edition, Rev. No. 3).

3.5. Each pipe is subjected to a hydraulic pressure test. With 100% quality control of the weld by non-destructive methods, hydraulic pressure testing may not be carried out. At the same time, the ability of the pipes to withstand the test hydraulic pressure is guaranteed.

(Revised edition, Rev. No. 6).

3.6. To check the thickness of the zinc coating on the outer surface and in accessible places on the inner surface, two pipes are taken from the lot.

(Revised edition, Rev. No. 2).

3.7. If unsatisfactory test results are obtained for at least one of the indicators, a second test is carried out on a double sample.

The retest results apply to the entire lot.

4. TEST METHODS

4.1. For quality control, one sample is cut from each selected pipe for each type of test.

The tensile test is carried out according to GOST 10006. Instead of tensile testing, it is allowed to control mechanical properties by non-destructive methods.

(Changed edition, Rev. No. 3, 6).

4.2. Inspection of the surface of the pipes is carried out visually.

4.3. Hydraulic testing is carried out in accordance with GOST 3845 with exposure under test pressure for at least 5 s.

4.4. The bend test is carried out according to GOST 3728. Galvanized pipes are tested before coating.

(Revised edition, Rev. No. 3).

4.4a. The expansion test is carried out according to GOST 8694 on a conical mandrel with a taper angle of 6°.

The test can be carried out on a mandrel with a taper angle of 30°.

(Changed edition, Rev. No. 3, 4).

4.4b. The flattening test is carried out according to GOST 8695.

(Revised edition, Rev. No. 3).

4.4c. The control of the weld is carried out by non-destructive methods according to the normative and technical documentation.

(Introducedadditionally, ch. No. 3).

4.5. The thickness of the zinc coating on the outer surface and in accessible places on the inner surface is controlled in accordance with GOST 9.301 and GOST 9.302, as well as with devices of the MT-41NTs, MTZON or Impulse types according to the regulatory and technical documentation.

4.6. The thread is checked with threaded ring gauges according to GOST 2533 (third class of accuracy).

In this case, the screwing of the non-going gauge-ring on the thread should be no more than three turns.

(Changed edition, Rev. No. 3, 4).

4.7. The curvature of the pipes is controlled by a straightedge according to GOST 8026 and a set of probes according to NTD.

(Changed edition, Rev. No. 3, 5).

4.8. The right angle of the ends of the pipes is controlled by a 90 ° square with a size of 160x100 mm class 3 GOST 3749, plate probes of set 4 according to NTD or a goniometer

Designation:	GOST 3262-75*
Russian name:	Pipes steel water and gas. Specifications
Status:	current
Replaces:	GOST 3262-62
Text update date:	01.10.2008
Date added to database:	01.02.2009
Date of entry into force:	01.01.1977
Designed by:	USSR Ministry of Ferrous Metallurgy
Approved:	USSR State Committee for Standards (09/11/1975)
Published:	Standards Publishing House No. 1994

STEEL PIPES

SPECIFICATIONS

GOST 3262-75

STANDARDS PUBLISHING HOUSE

Moscow

STATE STANDARD OF THE UNION OF THE SSR

the dateintroductions 01.01.77

This standard applies to non-galvanized and galvanized steel welded pipes with cut or knurled cylindrical threads and without threads used for water and gas pipelines, heating systems, as well as for parts of water and gas pipeline structures.

1. ASSORTMENT

1.1. Pipes are made according to the dimensions and weight given in Table. one.

At the request of the consumer, light series pipes intended for thread rolling are manufactured according to the mass dimensions given in Table. 2.

(Changed edition, Rev. No. 1 , 3 ).

1.2. The length of the pipe is made from 4 to 12 m:

measured or multiple measured length with an allowance for each cut of 5 mm and a maximum deviation for the entire length plus 10 mm;

unmeasured length.

By agreement between the manufacturer and the consumer, up to 5% of pipes with a length of 1.5 to 4 m are allowed in a batch of off-gauge pipes.

Table 1

Dimensions, mm

Conditional pass	Outside diameter	Pipe Wall Thickness			Weight of 1 m of pipes, kg
Conditional pass	Outside diameter		ordinary	enhanced		ordinary	enhanced

table 2

Dimensions, mm

Conditional pass	Outside diameter	Wall thickness	Weight of 1 m of pipes, kg

Notes:

1. For a thread made by knurling, a reduction in its internal diameter of up to 10% along the entire length of the thread is allowed on the pipe.

2. The mass of 1 m of pipes was calculated with a steel density of 7.85 g / cm 3. Galvanized pipes are 3% heavier than non-galvanized ones.

1.3. Limit deviations in pipe dimensions should not exceed those indicated in Table. 3.

Table 3

Pipe dimensions	Limit deviations for manufacturing precision pipes
		elevated
Outer diameter with nominal bore:
up to 40 mm incl.
	- 0,5
Outer diameter with nominal bore: over 40 mm
	- 1,0
Wall thickness	- 15 %	- 10 %

Notes :

1. The maximum deviation in the plus side along the wall thickness is limited by the maximum deviations in the mass of pipes.

2. Pipes of the usual manufacturing accuracy are used for water supply, gas pipelines and system heating. Pipes of increased manufacturing accuracy are used for parts of water and gas pipeline structures.

1.4. Maximum deviations in the mass of pipes should not exceed + 8%.

At the request of the consumer, the maximum deviations in mass should not exceed:

7.5% - for the party;

10% - for a single pipe.

(Changed edition, Rev. No. 2, 5).

1.5. The curvature of pipes per 1 m of length should not exceed:

2 mm - with nominal bore up to 20 mm inclusive;

1.5 mm - with nominal bore over 20 mm.

1.6. Pipe threads can be long or short. Thread requirements must comply with those specified in Table. 4.

Table4

Conditional passage, mm	Thread length to the run, mm		Conditional passage, mm	Number of threads with conditional passage	Thread length to the run, mm
Conditional passage, mm		short	Conditional passage, mm	Number of threads with conditional passage		short

1.7. Pipes with a nominal bore of 6, 8, 10, 15 and 20 mm are wound into coils at the request of the consumer.

Legend examples

Ordinary pipe, not galvanized, of the usual manufacturing accuracy, random length, with a nominal bore of 20 mm, a wall thickness of 2.8 mm, without thread and without a coupling:

Trumpet 20´ 2.8 GOST 3262-75

The same with the clutch:

Pipe M-20´ 2.8 GOST 3262-75

The same, measured length, threaded:

Pipe R-20´ 2.8 - 4000 GOST 3262-75

The same, zinc coated, random length, threaded:

Pipe Ts-R-20´ 2.8 GOST 3262-75

The same, with zinc coating, measured length, threaded:

Pipe Ts-R-20´ 2.8 - 4000 GOST 3262-75

For pipes for thread rolling, the letter H is indicated after the word "pipe" in the symbol.

For pipes with a long thread, the letter D is indicated after the word "pipe" in the symbol.

For pipes of increased manufacturing accuracy, the letter P is indicated in the symbol after the nominal bore size.

(Revised edition, Rev. No. 1).

2. TECHNICAL REQUIREMENTS

2.1. Pipes are manufactured in accordance with the requirements of this standard and according to technological regulations approved in the prescribed manner, from steels according to GOST 380 and GOST 1050 without standardization of mechanical properties and chemical composition.

Pipes for parts of water supply and gas pipeline structures are made of steel according to GOST 1050.

2.2. At the request of the consumer, the ends of pipes to be welded with a wall thickness of 5 mm or more must be chamfered at an angle of 35-40 ° to the end of the pipe. At the same time, an end ring with a width of 1 - 3 mm should be left.

At the request of the consumer, on ordinary and reinforced pipes with a nominal bore of more than 10 mm, the thread is applied to both ends of the pipe.

2.1; 2.2. (Changed edition, Rev. No. 3, 4).

2.3. At the request of the consumer, the pipes are equipped with couplings made in accordance with GOST8944, GOST8954, GOST8965 and GOST8966 at the rate of one coupling for each pipe.

(Revised edition, Rev. No. 3).

2.4. Cracks, captivity, swelling and sunsets are not allowed on the surface of the pipes.

Laminations are not allowed at the ends of the pipes.

On pipes made by furnace welding, it is allowed to reduce the outer diameter to 0.5 mm at the weld site if there is a gentle thickening of the inner diameter of not more than 1.0 mm in this place.

(Changed edition, Rev. No. 3, 4).

(Changed edition, Rev. No. 2, 3, 4, 5, 6).

2.6. Pipe ends must be cut square. The value of the bevel of the end is allowed no more than 2 ° . Burr residue must not exceed 0.5 mm. When removing burrs, the formation of blunting (rounding) of the ends is allowed. It is allowed to cut pipes in the line of the mill.

By agreement between the manufacturer and the consumer, burrs up to 1 mm are allowed on pipes with a nominal bore of 6-25 mm, made by furnace welding.

(Changed edition, Rev. No. 4, 6).

2.7. Galvanized pipes must have a continuous zinc coating over the entire surface with a thickness of at least 30 microns. The absence of zinc coating on the ends and threads of pipes is allowed.

On the surface of galvanized pipes, blistering and foreign inclusions (hardzinc, oxides, sintered charge), peeling of the coating from the base metal are not allowed.

Separate flux spots and traces of pipe capture by lifting devices, roughness and slight local zinc deposits are allowed.

It is allowed to correct individual non-galvanized sections by 0.5% of the outer surface of the pipe in accordance with GOST 9.307.

(Changed edition, Rev. No. 3, 4).

2.8. Pipes must withstand hydraulic pressure:

2.4 MPa (25 kgf / cm 2) - pipes, ordinary and light;

3.1 MPa (32 kgf / cm 2) - reinforced pipes.

At the request of the consumer, the pipes must withstand a hydraulic pressure of 4.9 MPa (50 kgf / cm 2)

At the request of the consumer, the pipes must withstand the expansion test:

for pipes with conditional passage from 15 to 50 mm - not less than 7%;

for pipes with a nominal bore of 65 or more - at least 4%.

At the request of the consumer, the pipes must withstand the flattening test up to a distance between the flattened surfaces equal to 2/3 of the outer diameter of the pipes.

2.8,2.9. (Changed edition, Rev. No. 2, 3, 5).

2.10. At the request of the consumer, the mechanical properties of pipes for parts of water and gas pipeline structures must comply with GOST 1050.

2.11. The pipe thread must be clean, free of flaws and burrs and comply with GOST 6357, accuracy class B.

Pipes with cylindrical threads are used when assembling with seals.

2.10; 2.11. (Changed edition, Rev. No. 3, 4).

2.13. It is allowed on the thread to reduce the useful length of the thread (without run-off) up to 15% compared to that specified in, and at the request of the consumer up to 10%.

2.12.,2.13. (Changed edition, Rev. No. 2, 3, 5).

2.14. Threading galvanized pipes is carried out after galvanizing.

2.15. (Deleted, Rev. No. 3).

2.16. At the request of the consumer, welded seams of pipes are subjected to control by non-destructive methods.

(Revised edition, Rev. No. 5).

3. ACCEPTANCE RULES

3.1. Pipes are accepted in batches. The batch must consist of pipes of the same size, of the same brand and be accompanied by one quality document in accordance with GOST 10692 with an addition for pipes intended for the manufacture of parts for water and gas pipeline structures, made of steel according to GOST1050: chemical composition and mechanical properties of steel in accordance with the document on the quality of the blank manufacturer.

The mass of the party is not more than 60 tons.

(Changed edition, Rev. No. 3, 4).

3.2. Surface, dimensions and curvature are checked for each pipe of the batch.

It is allowed to use statistical control methods according to GOST 18242 with a normal level. Control plans are established by agreement between the manufacturer and the consumer.

The control of the outer diameter of the pipes is carried out at a distance of at least 15 mm from the end of the pipe.

(Changed edition, Rev. No. 3, 4, 5).

3.3. To control the parameters of the thread, to test for expansion, flattening, bending, the height of the internal burr, burr residue, right angle and chamfer angle (for pipes with beveled edges), mechanical properties, no more than 1%, but not less than two pipes from the batch, are selected, and for pipes made by continuous furnace welding - two pipes per batch.

(Changed edition, Rev. No. 3, 4).

3.4. All pipes are subjected to mass control.

(Revised edition, Rev. No. 3).

(Revised edition, Rev. No. 6).

3.6. To check the thickness of the zinc coating on the outer surface and in accessible places on the inner surface, two pipes are taken from the batch.

(Revised edition, Rev. No. 2).

3.7. If unsatisfactory test results are obtained for at least one of the indicators, a second test is carried out on a double sample.

The results of repeated tests apply to the entire batch.

4. TEST METHODS

4.1. For quality control, one sample is cut from each selected pipe for each type of test.

The tensile test is carried out according to GOST 10006. Instead of the tensile test, it is allowed to control the mechanical properties by non-destructive methods.

4.2. Inspection of the surface of the pipes is carried out visually.

4.3. Hydraulic testing is carried out according to GOST 3845 with exposure under test pressure for at least 5 s.

4.4. The bend test is carried out according to GOST 3728. Galvanized pipes are tested before coating.

(Revised edition, Rev. No. 3).

4.4a. The expansion test is carried out according to GOST 8694 on a conical mandrel with a taper angle of 6 ° .

It is allowed to test on a mandrel with a taper angle of 30 ° .

(Changed edition, Rev. No. 3, 4).

4.4b. The flattening test is carried out according to GOST 8695.

(Revised edition, Rev. No. 3).

4.4c. Weld seam control is carried out by non-destructive methods according to normative and technical documentation.

(Introduced additionally, Rev. No. 3).

4.6. The thread is checked with threaded ring gauges according to GOST 2533 (third class of accuracy).

In this case, the screwing-in of the non-going ring gauge on the thread should be no more than three turns.

(Changed edition, Rev. No. 3, 4).

4.7. The curvature of the pipes is controlled by a straightedge in accordance with GOST 8026 and a set of probes according to ND.

(Changed edition, Rev. No. 3, 5).

4.8. The right angle of the ends of the pipes is controlled by a square 90 ° size 160´ 100 mm class 3 GOST 3749, plate probes of set 4 according to ND or goniometer GOST 5378. The bevel angle is controlled by a goniometer according to GOST 5378.

(Changed edition, Rev. No. 3, 6).

4.9. The control of the outer diameter is carried out with smooth micrometers in accordance with GOST 6507, with staple gauges in accordance with GOST 2216 or GOST 18360.

The wall thickness, the height of the internal burr and the height of the burrs are measured with a micrometer according to GOST 6507-90 or a wall gauge according to GOST 11358 from both ends of the pipe.

The length of the pipes is measured with a tape measure according to GOST 7502. The thread is controlled by gauges according to GOST 2533.

Control of the mass of a batch of pipes is carried out on scales of not more than 10 tons with a division value of not more than 20 kg.

(Changed edition, Rev. No. 3, 4, 5, 6).

4.10. Weld seam control is carried out by non-destructive methods according to technical documentation.

(Introduced additionally, Rev. No. 4).

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

5.1. Marking, packaging, transportation and storage are carried out in accordance with GOST 10692 with an addition.

5.1.1. The pipe thread must be protected from mechanical damage and corrosion by lubricant according to the normative and technical documentation.

Sec. 5. (Revised edition, Rev. No. 3).

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Ferrous Metallurgy of the USSR

DEVELOPERS

V. I. Strzhok, cand. tech. Sciences, V. M. Vorona, Ph.D. tech. Sciences, Yu. M. Mironov, cand. tech. nook, A. I. Postolova

2. APPROVED AND INTRODUCED BY Decree of the State Committee of the USSR on Standards dated September 11, 1975 No. 2379

3. Periodicity of inspection 5 years

4. REPLACE GOST3262-62

5. REFERENCE REGULATIONS AND TECHNICAL DOCUMENTS

	Item number
GOST 9.301-86
GOST 9.302-88
GOST 9.307-89
GOST 380- 94
GOST 1050-88
GOST 2216-84
GOST 2533-88
GOST 3728-78
GOST 3749-77
GOST 3845-75
GOST 5378-88
GOST 6357-81
GOST 6507-90
GOST 7502-89
GOST 8026-92
GOST 8694-75
GOST 8695-75
GOST 8944-75
GOST 8954-75
GOST 8965-75
GOST 8966-75
GOST 10006-80
GOST 10692-80
GOST 11358-89
GOST 18242-72
GOST 18360-9 3

6. The validity period was removed by the Decree of the State Standard of November 12, 1991 No. 1726

7. Reprinted with Amendments No. 1, 2, 3, 4, 5, 6, approved in November 1977, December 1978, January 1987, May 1988, November 1989, November 1991 (IUS 1 -78.2-79, 4-87, 8-88, 2-90, 2-92)

Water-supply and gas-supply steel pipes. Specifications

GOST 3262-75

OKP 13 8500, OKP 13 8501

Introduction date 01.01.77

(Changed edition, Rev. No. 2, 3, 5).

1. ASSORTMENT

1.1. Pipes are made according to the dimensions and weight given in table. one.

At the request of the consumer, light series pipes intended for thread rolling are manufactured according to the dimensions and weight given in Table. 2.

(Changed edition, Rev. No. 1, 3).

1.2. The length of the pipe is made from 4 to 12 m:

measured or multiple measured length with an allowance for each cut of 5 mm and a longitudinal deviation for the entire length plus 10 mm;

unmeasured length.

By agreement between the manufacturer and the consumer, up to 5% of pipes with a length of 1.5 to 4 m are allowed in a batch of off-gauge pipes.

Table 1

Table 2

N o t e s:

1. For a thread made by knurling, a reduction in its inner diameter of up to 10% along the entire length of the thread is allowed on the pipe.

2. The mass of 1 m of pipes is calculated with a steel density of 7.85 g / cm 3. Galvanized pipes are 3% heavier than non-galvanized ones.

1.3. Limit deviations in pipe dimensions should not exceed those indicated in Table. 3.

Table 3

N o t e s:

1. The maximum deviation in the plus side along the wall thickness is limited by the maximum deviations in the mass of pipes.

2. Pipes of ordinary manufacturing accuracy are used for water pipes, gas pipelines and heating systems. Pipes of increased manufacturing accuracy are used for parts of water and gas pipeline structures.

1.4. Maximum deviations in the mass of pipes should not exceed +8%.

At the request of the consumer, the maximum deviations in mass should not exceed:

7.5% - for the party;

10% - for a single pipe.

(Changed edition, Rev. No. 2, 5).

1.5. The curvature of pipes per 1 m of length should not exceed:

2 mm - with nominal bore up to 20 mm inclusive;

1.5 mm - with nominal bore over 20 mm.

1.6. Pipe threads can be long or short. Thread requirements must comply with those specified in table. 4.

Table 4

1.7. Pipes with a nominal bore of 6, 8, 10, 15 and 20 mm are wound in coils at the request of the consumer.

EXAMPLES OF CONVENTIONS

Ordinary pipe, non-galvanized, of the usual manufacturing accuracy, random length, with a nominal bore of 20 mm, a wall thickness of 2.8 mm, without thread and without a coupling:

Pipe 20 -2.8 TOAST 3262-75

The same with the clutch:

Pipe M-20 -2.8 TOST 3262-75

The same, measured length, threaded:

Pipe R-20 2.8-4000 TOST 3262-75

The same, zinc coated, random length, threaded:

Pipe Ts-R-20 -2.8 TOST 3262-75

The same, with zinc coating, measured length, with thread:

Pipe Ts-R-20 -2.8-4000 TOST 3262-75

For pipes for thread rolling, the letter H is indicated after the word "pipe" in the symbol.

For pipes with a long thread, the letter D is indicated after the word "pipe" in the symbol.

For pipes of increased manufacturing accuracy, the letter P is indicated in the symbol after the nominal bore size.

(Revised edition, Rev. No. 1).

2. TECHNICAL REQUIREMENTS

2.1. Pipes are manufactured in accordance with the requirements of this standard and according to the technological regulations approved in the prescribed manner, from steels in accordance with GOST 380 and GOST 1050 without standardization of mechanical properties and chemical composition.

Pipes for parts of water and gas pipeline structures are made of steel according to GOST 1050.

2.2. At the request of the consumer, the ends of pipes to be welded with a wall thickness of 5 mm or more must be chamfered at an angle of 35-40 ° to the end of the pipe. In this case, an end ring with a width of 1-3 mm should be left.

At the request of the consumer, on ordinary and reinforced pipes with a nominal bore of more than 10 mm, the thread is applied to both ends of the pipe.

2.1, 2.2. (Changed edition, Rev. No. 3, 4).

2.3. At the request of the consumer, the pipes are equipped with couplings made in accordance with GOST 8944, GOST 8954, GOST 8965 and GOST 8966, at the rate of one coupling for each pipe.

(Revised edition, Rev. No. 3).

2.4. Cracks, captivity, swelling and sunsets are not allowed on the surface of the pipes.

At the ends of the pipes, delamination is not allowed.

On pipes made by furnace welding, it is allowed to reduce the outer diameter to 0.5 mm at the weld site if there is a gentle thickening of the inner diameter of not more than 1.0 mm in this place.

(Changed edition, Rev. No. 3, 4).

(Changed edition, Rev. No. 2, 3, 4, 5, 6).

2.6. Pipe ends must be cut square. The value of the bevel of the end face is not more than 2°. Burr residues should not exceed 0.5 mm. When removing burrs, the formation of blunting (rounding) of the ends is allowed. It is allowed to cut pipes in the mill line.

By agreement between the manufacturer and the consumer, burrs up to 1 mm are allowed on pipes with a nominal bore of 6-25 mm, made by furnace welding.

(Changed edition, Rev. No. 4, 6).

2.7. Galvanized pipes must have a continuous zinc coating over the entire surface with a thickness of at least 30 microns. The absence of zinc coating on the ends and threads of pipes is allowed.

On the surface of galvanized pipes, blistering and foreign inclusions (hardzinc, oxides, sintered charge), peeling of the coating from the base metal are not allowed.

Separate flux spots and traces of pipes being caught by lifting devices, roughness and slight local zinc deposits are allowed.

It is allowed to correct individual non-galvanized sections by 0.5% of the outer surface of the pipe in accordance with GOST 9.307.

(Changed edition, Rev. No. 3, 4).

2.8. Pipes must withstand hydraulic pressure:

2.4 MPa (25 kgf / cm 2) - ordinary and light pipes;

3.1 MPa (32 kgf / cm 2) - reinforced pipes.

At the request of the consumer, the pipes must withstand a hydraulic pressure of 4.9 MPa (50 kgf / cm 2).

At the request of the consumer, the pipes must withstand the expansion test:

for pipes with nominal bore from 15 to 50 mm - not less than 7%;

for pipes with a nominal bore of 65 mm or more - at least 4%.

At the request of the consumer, the pipes must withstand the flattening test up to a distance between flattened surfaces equal to 2/3 of the outer diameter of the pipes.

2.8, 2.9. (Changed edition, Rev. No. 2, 3, 5).

2.10. At the request of the consumer, the mechanical properties of pipes for parts of water supply and gas pipeline structures must comply with GOST 1050.

2.11. The pipe thread must be clean, without flaws and burrs, and comply with GOST 6357, accuracy class B.

Pipes with cylindrical threads are used when assembling with seals.

2.10, 2.11. (Changed edition, Rev. No. 3, 4).

2.12. In the place of the seam, blackness is allowed on the threads of the thread, if the decrease in the normal height of the thread profile does not exceed 15%, and at the request of the consumer does not exceed 10%.

Threads with stripped (for cut) or incomplete (for knurled) threads are allowed on threads, provided that their total length does not exceed 10% of the required thread length, and at the request of the consumer does not exceed 5%.

2.13. It is allowed on the thread to reduce the useful length of the thread (without run-off) up to 15% compared to that indicated in Table. 4, and at the request of the consumer - up to 10%.

2.12, 2.13. (Changed edition, Rev. No. 2, 3, 5).

2.14. Threading on galvanized pipes is carried out after galvanizing.

2.15. (Deleted, Rev. No. 3).

2.16. At the request of the consumer, pipe welds are subjected to control by non-destructive methods.

(Revised edition, Rev. No. 5).

3. ACCEPTANCE RULES

3.1. Pipes are accepted in batches. The batch must consist of pipes of the same size, one brand steel and be accompanied by one quality document in accordance with GOST 10692 with an addition for pipes intended for the manufacture of parts for water and gas pipeline structures, made of steel in accordance with GOST 1050; the chemical composition and mechanical properties of steel - in accordance with the document on the quality of the enterprise - the manufacturer of the workpiece.

Party weight - no more than 60 tons.

(Changed edition, Rev. No. 3, 4).

3.2. The surface, dimensions and curvature are checked for each pipe of the batch.

It is allowed to apply statistical control methods according to GOST 18242 with a normal level. Control plans are established by agreement between the manufacturer and the consumer.

The control of the outer diameter of the pipes is carried out at a distance of at least 15 mm from the end of the pipe.

(Changed edition, Rev. No. 3, 4, 5).

3.3. To control the parameters of the thread, to test for expansion, flattening, bending, the height of the internal burr, burr residues, right angle and chamfer angle (for pipes with bevelled edges), mechanical properties, no more than 1%, but not less than two pipes from the batch, are selected, and for pipes manufactured by continuous furnace welding - two pipes from the batch.

(Changed edition, Rev. No. 3, 4).

3.4. All pipes are subjected to weight control.

(Revised edition, Rev. No. 3).

(Revised edition, Rev. No. 6).

3.6. To check the thickness of the zinc coating on the outer surface and in accessible places on the inner surface, two pipes are taken from the lot.

(Revised edition, Rev. No. 2).

3.7. Upon receipt of unsatisfactory test results for at least one of the indicators, it is repeated tests on a double sample.

The retest results apply to the entire lot.

4. TEST METHODS

4.1. For quality control, one sample is cut from each selected pipe for each type of test.

The tensile test is carried out in accordance with GOST 10006. Instead of the tensile test, it is allowed to control the mechanical properties by non-destructive methods.

4.2. Inspection of the surface of the pipes is carried out visually.

4.3. Hydraulic testing is carried out in accordance with GOST 3845 with exposure under test pressure for at least 5 s.

4.4. The bend test is carried out according to GOST 3728. Galvanized pipes are tested before coating.

(Revised edition, Rev. No. 3).

4.4a. The expansion test is carried out according to GOST 8694 on a conical mandrel with a taper angle of 6°.

The test can be carried out on a mandrel with a taper angle of 30°.

(Changed edition, Rev. No. 3, 4).

4.46. The flattening test is carried out according to GOST 8695.

(Revised edition, Rev. No. 3).

4.4c. Weld seam control is carried out by non-destructive methods according to normative documentation.

(Introduced additionally, Rev. No. 3).

4.5. The thickness of the zinc coating on the outer surface and in accessible places on the inner surface is controlled in accordance with GOST 9.301 and GOST 9.302, as well as with devices of the MT-41NTs, MTZON types or the Impulse type according to regulatory documentation.

4.6. The thread is checked with threaded ring gauges according to GOST 2533 (third class of accuracy).

In this case, the screwing of the non-going gauge-ring on the thread should be no more than three turns.

(Changed edition, Rev. No. 3, 4).

4.7. The curvature of the pipes is controlled by a straightedge in accordance with GOST 8026 and a set of probes according to ND.

(Changed edition, Rev. No. 3, 5).

4.8. The right angle of the ends of the pipes is controlled by a 90 ° square with a size of 160 100 mm of class 3 according to GOST 3749, plate probes of set 4 according to ND or a goniometer according to GOST 5378. The bevel angle is controlled by a goniometer according to GOST 5378.

(Changed edition, Rev. No. 3, 6).

4.9. The control of the outer diameter is carried out with smooth micrometers in accordance with GOST 6507, with staple gauges in accordance with GOST 2216 or GOST 18360.

The wall thickness, the height of the internal burr and the height of the burrs are measured with a micrometer according to GOST 6507 or a wall gauge according to GOST 11358 from both ends of the pipe.

The length of the pipes is measured with a tape measure in accordance with GOST 7502. The thread is controlled with gauges in accordance with GOST 2533.

The control of the mass of a batch of pipes is carried out on scales of not more than 10 tons with a division value of not more than 20 kg.

(Changed edition, Rev. No. 3, 4, 5, 6).

4.10. Weld seam control is carried out by non-destructive methods according to technical documentation.

(Introduced additionally, Rev. No. 4).

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

5.1. Marking, packaging, transportation and storage are carried out in accordance with GOST 10692 with an addition.

5.1.1. Pipe threads must be protected from mechanical damage and corrosion by lubricant according to normative documentation.

Sec. 5. (Changed edition, Rev. No. 3).

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Ferrous Metallurgy of the USSR DEVELOPERS

V. I. Strizhok, Ph.D. tech. sciences; V. M. Vorona, Ph.D. tech. sciences; Yu. M. Mironov, Ph.D. tech. sciences; A. I. Postolova

2. APPROVED AND INTRODUCED BY Decree of the USSR State Committee for Standards dated 11.09.75 No. 2379

3. Periodicity of inspection - 5 years

4. REPLACE GOST 3262-62

5. REFERENCE REGULATIONS AND TECHNICAL DOCUMENTS

6. The validity period was removed by the Decree of the State Standard of November 12, 1991 No. 1726

7. EDITION with Amendments No. 1, 2, 3, 4, 5, 6, approved January 1987, May 1988, November 1989, November 1991 2-90, 2-92)

On the territory of the Russian Federation, GOST R 50779.71-99 applies.

IT, electronics and home appliances
Extraction and processing
Manufacturing and construction
Industry
Machinery and equipment
General provisions
Services, management and sociology
Mathematics, natural sciences
healthcare
environmental protection
Metrology and measurements. physical phenomena.
Tests.
Imaging technology.
Precise mechanics. Jewelry business.

Categories of OKS in expanded form

Classifier OKPD 2

search code OKPD 2 online, all categories of the classifier

Conventions

File Icons and Document Properties- GOST icon;

File types

- the document is represented by a set of scanned images; - the document can be downloaded as one PDF file, the file consists of unrecognized scanned pages; - the document can be downloaded as one PDF file with recognized text; - the document can be downloaded as one PDF file, links to other GOSTs work inside the file, the text is recognized

GOST statuses

- the document is currently valid (GOST status - current); - the document has been canceled (GOST status - Canceled); - the document has been replaced (GOST status - Replaced); - GOST is not valid on the territory of the Russian Federation;

GOST 3262-75 Steel water and gas pipes. Specifications

Categories GOST 3262-75 for OKS:

23.40. Pipelines and their components
23.40.10 Cast iron and steel pipes *Steel pipes and tubes for special purposes, see 77.140.75

Document status: valid, put into effect on 01/01/1977 Title in English: Water-supply and gas-supply steel pipes. Specifications Date of updating information according to the standard: 09/11/2019 at 10:56 am (less than 3 months ago) Type of standard: Standards for products (services) GOST start date: 1977-01-01 Date of last edition of the document: 2007-05-01

Document codes GOST 3262-75:

OKP code: 138500;138501 KGS code: B62 OKSTU code: 1385

Number of pages: 8

Purpose of GOST 3262-75: This standard applies to non-galvanized and galvanized steel welded pipes with threaded or knurled cylindrical threads and without threads used for water and gas pipelines, heating systems, as well as for parts of water and gas pipeline structures

SRNTI index(es): 534731 The document was developed by the organization: Minchermet of the USSR Document keywords: tests, acceptance, assortment, technical requirements, non-galvanized pipes, galvanized pipes, welded pipes, steel pipes

Links to others: TU 2-034-225-88

You can download GOST 3262-75 in the following versions:

Date added in file version:

Amendments and changes to GOST 3262-75:

Name, type:

registrations:

start action:

Change No. 1 to GOST 3262-75

change type: Text change
Change number: 1
Registration number: 2669

Change No. 2 to GOST 3262-75

change type: Text change
Change number: 2
Registration number: 45

Change No. 3 to GOST 3262-75

change type: Text change; Title changed
Change number: 3
Registration number: 4456
New value: See title

Change No. 4 to GOST 3262-75

change type: Text change
Change number: 4
Registration number: 1139
New value: -

Change No. 5 to GOST 3262-75

change type: Text change
Change number: 5
Registration number: 3347
New value: -

Change No. 6 to GOST 3262-75

change type: Text change
Change number: 6
Registration number: 1726
New value: -

GOST 3262-75

Group B62

INTERSTATE STANDARD

STEEL WATER AND GAS PIPES

Specifications

Water-supply and gas-supply steel pipes. Specifications

OKP 13 8500, OKP 13 8501

Introduction date 1977-01-01

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Ferrous Metallurgy of the USSR

DEVELOPERS

V.I.Struzhok, Ph.D. tech. sciences; V.M.Vorona, Ph.D. tech. sciences; Yu.M.Mironov, Ph.D. tech. sciences; A.I. Postolova

2. APPROVED AND INTRODUCED BY Decree of the USSR State Committee for Standards dated 11.09.75 N 2379

3. Periodicity of inspection - 5 years

4. REPLACE GOST 3262-62

5. REFERENCE REGULATIONS AND TECHNICAL DOCUMENTS


	Item number

________________
* Valid on the territory of the Russian Federation.

6. The limitation of the validity period was removed by the Decree of the State Standard of November 12, 1991 N 1726

7. EDITION with Changes N 1, 2, 3, 4, 5, 6, approved in November 1977, December 1978, January 1987, May 1988, November 1989, November 1991 ( IUS 1-78, 2-79, 4-87, 8-88, 2-90, 2-92)

(Changed edition, Rev. N 2, 3, 5).

1. ASSORTMENT

1.1. Pipes are made according to the dimensions and weight given in table.1.

Table 1

Dimensions, mm


Conditional pass	Outside diameter	Pipe Wall Thickness			Weight of 1 m of pipes, kg
		lungs	ordinary	enhanced	lungs	ordinary	enhanced

At the request of the consumer, light series pipes intended for thread rolling are manufactured according to the dimensions and weight given in Table 2.

table 2

Dimensions, mm


Conditional pass	Outside diameter	Wall thickness	Weight of 1 m of pipes, kg

Notes:

1. For a thread made by knurling, a reduction in its inner diameter of up to 10% along the entire length of the thread is allowed on the pipe.

2. The mass of 1 m of pipes is calculated with a steel density of 7.85 g/cm. Galvanized pipes are 3% heavier than non-galvanized ones.

(Changed edition, Rev. N 1, 3).

1.2. The length of the pipe is made from 4 to 12 m:

Measured or multiple measured length with an allowance for each cut of 5 mm and a longitudinal deviation for the entire length plus 10 mm;

Unmeasured length.

By agreement between the manufacturer and the consumer, up to 5% of pipes with a length of 1.5 to 4 m are allowed in a batch of off-gauge pipes.

1.3. Limit deviations in pipe dimensions should not exceed those indicated in Table 3.

Table 3


Pipe size	Limit deviation for precision pipes manufacturing
		elevated
Outer diameter with nominal bore:
up to 40 mm incl.	0.4mm -0,5
over 40 mm	0,8% -1,0
Wall thickness

Notes:

1. The maximum deviation in the plus side along the wall thickness is limited by the maximum deviations in the mass of pipes.

1.4. Maximum deviations in the mass of pipes should not exceed + 8%.

At the request of the consumer, the maximum deviations in mass should not exceed:

7.5% - for the party;

10% - for a single pipe.

(Changed edition, Rev. N 2, 5).

1.5. The curvature of pipes per 1 m of length should not exceed:

2 mm - with nominal bore up to 20 mm inclusive;

1.5 mm - with nominal bore over 20 mm.

1.6. Pipe threads can be long or short. Thread requirements must be as specified in Table 4.

Table 4


Conditional passage, mm	Number of threads with conditional passage	Thread length to the run, mm
			short

1.7. Pipes with a nominal bore of 6, 8, 10.15 and 20 mm are wound into coils at the request of the consumer.

Legend Examples

Ordinary pipe, non-galvanized, of the usual manufacturing accuracy, random length, with a nominal bore of 20 mm, a wall thickness of 2.8 mm, without thread and without a coupling:

Pipe 20x2.8 GOST 3262-75

The same with the clutch:

Pipe M-20x2.8 GOST 3262-75

The same, measured length, threaded:

Pipe P-20x2.8-4000 GOST 3262-75

The same, zinc coated, random length, threaded:

Pipe Ts-R-20x2.8 GOST 3262-75

The same, with zinc coating, measured length, with thread:

Pipe Ts-R-20x2.8-4000 GOST 3262-75

For pipes for thread rolling, the letter H is indicated after the word "pipe" in the symbol.

For pipes with a long thread, the letter D is indicated after the word "pipe" in the symbol.

For pipes of increased manufacturing accuracy, the letter P is indicated in the symbol after the nominal bore size.

(Changed edition, Rev. N 1).

2. TECHNICAL REQUIREMENTS

2.1. Pipes are manufactured in accordance with the requirements of this standard and according to the technological regulations approved in the prescribed manner, from steels with and without standardization of mechanical properties and chemical composition.

Pipes for parts of water and gas pipeline structures are made of steel according to GOST 1050.

2.2. At the request of the consumer, at the ends of pipes to be welded, with a wall thickness of 5 mm or more, chamfers must be removed at an angle of 35-40 ° to the end of the pipe. In this case, an end ring with a width of 1-3 mm should be left.

At the request of the consumer, on ordinary and reinforced pipes with a nominal bore of more than 10 mm, the thread is applied to both ends of the pipe.

2.1, 2.2. (Changed edition, Rev. N 3, 4).

2.3. At the request of the consumer, the pipes are equipped with couplings made according to, and, at the rate of one coupling for each pipe.

(Changed edition, Rev. N 3).

2.4. Cracks, captivity, swelling and sunsets are not allowed on the surface of the pipes.

At the ends of the pipes, delamination is not allowed.

On pipes made by furnace welding, it is allowed to reduce the outer diameter to 0.5 mm at the weld site if there is a gentle thickening of the inner diameter of not more than 1.0 mm in this place.

(Changed edition, Rev. N 3, 4).

(Changed edition, Rev. N 2, 3, 4, 5, 6).

By agreement between the manufacturer and the consumer, burrs up to 1 mm are allowed on pipes with a nominal bore of 6-25 mm, made by furnace welding.

(Changed edition, Rev. N 4, 6).

2.7. Galvanized pipes must have a continuous zinc coating over the entire surface with a thickness of at least 30 microns. The absence of zinc coating on the ends and threads of pipes is allowed.

On the surface of galvanized pipes, blistering and foreign inclusions (hardzinc, oxides, sintered charge), peeling of the coating from the base metal are not allowed.

Separate flux spots and traces of pipes being caught by lifting devices, roughness and slight local zinc deposits are allowed.

It is allowed to correct individual non-galvanized sections by 0.5% of the outer surface of the pipe in accordance with GOST 9.307.

(Changed edition, Rev. N 3, 4).

2.8. Pipes must withstand hydraulic pressure:

2.4 MPa (25 kgf / cm) - ordinary and light pipes;

3.1 MPa (32 kgf/cm) - reinforced pipes.

At the request of the consumer, the pipes must withstand a hydraulic pressure of 4.9 MPa (50 kgf/cm).

At the request of the consumer, the pipes must withstand the expansion test:

For pipes with nominal bore from 15 to 50 mm - not less than 7%;

For pipes with a nominal bore of 65 mm or more - at least 4%.

At the request of the consumer, the pipes must withstand the flattening test up to a distance between flattened surfaces equal to 2/3 of the outer diameter of the pipes.

2.8, 2.9. (Changed edition, Rev. N 2, 3, 5).

2.10. At the request of the consumer, the mechanical properties of pipes for parts of water and gas pipeline structures must comply with GOST 1050.

2.11. Pipe threads must be clean, free of flaws and burrs and comply with accuracy class B.

Pipes with cylindrical threads are used when assembling with seals.

2.10, 2.11. (Changed edition, Rev. N 3, 4).

2.13. It is allowed on the thread to reduce the useful length of the thread (without run-off) up to 15% compared to that indicated in Table 4, and at the request of the consumer - up to 10%.

2.12, 2.13. (Changed edition, Rev. N 2, 3, 5).

2.14. Threading on galvanized pipes is carried out after galvanizing.

2.15. (Deleted, Rev. N 3).

2.16. At the request of the consumer, welded seams of pipes are subjected to control by non-destructive methods.

(Changed edition, Rev. N 5).

3. ACCEPTANCE RULES

3.1. Pipes are accepted in batches. The batch must consist of pipes of the same size, the same steel grade and be accompanied by one quality document in accordance with the addendum for pipes intended for the manufacture of parts for water and gas pipeline structures, from steel according to; chemical composition and mechanical properties of steel - in accordance with the document on the quality of the enterprise - the manufacturer of the workpiece.

Party weight - no more than 60 tons.

(Changed edition, Rev. N 3, 4).

3.2. The surface, dimensions and curvature are checked for each pipe of the batch.

It is allowed to apply statistical control methods with a normal level. Control plans are established by agreement between the manufacturer and the consumer.

The control of the outer diameter of the pipes is carried out at a distance of at least 15 mm from the end of the pipe.

(Changed edition, Rev. N 3, 4, 5).

3.3. To control the parameters of the thread, to test for expansion, flattening, bending, the height of the internal burr, burr residues, right angle and chamfer angle (for pipes with bevelled edges), mechanical properties are selected no more than 1%, but not less than two pipes from the batch, and for pipes manufactured by continuous furnace welding, two pipes per lot.

(Changed edition, Rev. N 3, 4).

3.4. All pipes are subjected to weight control.

(Changed edition, Rev. N 3).

(Changed edition, Rev. N 6).

3.6. To check the thickness of the zinc coating on the outer surface and in accessible places on the inner surface, two pipes are taken from the lot.

(Changed edition, Rev. N 2).

3.7. Upon receipt of unsatisfactory test results for at least one of the indicators, it is repeated tests on a double sample.

The retest results apply to the entire lot.

4. TEST METHODS

4.1. For quality control, one sample is cut from each selected pipe for each type of test.

The tensile test is carried out in accordance with GOST 10006. Instead of the tensile test, it is allowed to control the mechanical properties by non-destructive methods.

4.2. Inspection of the surface of the pipes is carried out visually.

4.3. The hydraulic test is carried out with holding under test pressure for at least 5 s.

4.4. The bend test is carried out according to GOST 3728. Galvanized pipes are tested before coating.

(Changed edition, Rev. N 3).

4.4a. The expansion test is carried out on a conical mandrel with a taper angle of 6°.

The test can be carried out on a mandrel with a taper angle of 30°.

(Changed edition, Rev. N 3, 4).

4.4b. The flattening test is carried out according to GOST 8695.

(Changed edition, Rev. N 3).

4.4c. Weld seam control is carried out by non-destructive methods according to normative documentation.

(Introduced additionally, Rev. N 3).

4.5. The thickness of the zinc coating on the outer surface and in accessible places on the inner surface is controlled by and , as well as by devices of the MT-41NTs, MTZON or Impulse types according to regulatory documentation.

4.6. The thread is checked with threaded ring gauges according to (third accuracy class).

In this case, the screwing of the non-going gauge-ring on the thread should be no more than three turns.

(Changed edition, Rev. N 3, 4).

4.7. The curvature of the pipes is controlled by a straightedge along and a set of probes according to ND.

(Changed edition, Rev. N 3, 5).

4.8. The right angle of the ends of the pipes is controlled by a 90 ° square with a size of 160x100 mm of class 3 according to, lamellar probes of set 4 according to ND or a goniometer according to GOST 5378. The bevel angle of the chamfer is controlled by a goniometer according to GOST 5378.

(Changed edition, Rev. N 3, 6).

4.9. The control of the outer diameter is carried out with smooth micrometers according to, staple gauges according to or GOST 18360.

The wall thickness, the height of the internal burr and the height of the burrs are measured with a micrometer along or a wall gauge along at both ends of the pipe.

The length of the pipes is measured with a tape measure in accordance with GOST 7502. The thread is controlled with gauges in accordance with GOST 2533.

The control of the mass of a batch of pipes is carried out on scales of not more than 10 tons with a division value of not more than 20 kg.

(Changed edition, Rev. N 3, 4, 5, 6).

4.10. Weld seam control is carried out by non-destructive methods according to technical documentation.

(Introduced additionally, Rev. N 4).

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

5.1. Marking, packaging, transportation and storage are carried out according to the supplement.

5.1.1. Pipe threads must be protected from mechanical damage and corrosion by grease in accordance with regulatory documents.

Section 5. (Changed edition, Rev. N 3).

The text of the document is verified by:
official publication
Pipes metal and connecting parts to them.
Part 3. Welded pipes. Profile pipes: Sat. GOSTs. -
M.: IPK Standards Publishing House, 2001

INTERSTATE STANDARD

TECHNICAL CONDITIONS

Official edition

Standartinform

UDC 669.14-462:006.354

INTERSTATE

Group B62

STANDARD

STEEL WATER AND GAS PIPES

Specifications

Water-supply and gas-supply steel pipes. Specifications

MKS 23.040.10 OKP 13 8500, 13 8501

Introduction date 01.01.77

(Changed edition, Rev. No. 2, 3, 5).

1. ASSORTMENT

1.1. Pipes are made according to the dimensions and weight given in table. one.

At the request of the consumer, light series pipes intended for thread rolling are manufactured according to the dimensions and weight given in Table. 2.

(Changed edition, Rev. No. 1, 3).

1.2. The length of the pipe is made from 4 to 12 m:

measured or multiple measured length with an allowance for each cut of 5 mm and a longitudinal deviation for the entire length plus 10 mm;

unmeasured length.

By agreement between the manufacturer and the consumer, up to 5% of pipes with a length of 1.5 to 4 m are allowed in a batch of off-gauge pipes.

Official edition

Reprint prohibited

Dimensions, mm

Table 1

		Pipe Wall Thickness			Weight of 1 m of pipes, kg

Table 2 Dimensions, mm

Notes:

1. For a thread made by knurling, a reduction in its inner diameter of up to 10% along the entire length of the thread is allowed on the pipe.

2. The mass of 1 m of pipes is calculated with a steel density of 7.85 g / cm 3. Galvanized pipes are 3% heavier than non-galvanized ones.

1.3. Limit deviations in pipe dimensions should not exceed those indicated in Table. 3.

Table 3

Notes:

1. The maximum deviation in the plus side along the wall thickness is limited by the maximum deviations in the mass of pipes.

1.4. Maximum deviations in the mass of pipes should not exceed +8%.

At the request of the consumer, the maximum deviations in mass should not exceed:

7.5% - for the party;

10% - for a single pipe.

(Changed edition, Rev. No. 2, 5).

1.5. The curvature of pipes per 1 m of length should not exceed:

2 mm - with nominal bore up to 20 mm inclusive;

1.5 mm - with nominal bore over 20 mm.

1.6. Pipe threads can be long or short. Thread requirements must comply with those specified in table. 4.

Table 4

Conditional passage, mm	Thread length to the run, mm		Conditional passage, mm	Number of threads with conditional passage	Thread length to the run, mm
Conditional passage, mm		short	Conditional passage, mm	Number of threads with conditional passage		short

Pipes with a nominal bore of 6, 8, 10, 15 and 20 mm, at the request of the consumer, are wound into Examples of symbols

Ordinary pipe, non-galvanized, of the usual manufacturing accuracy, random length, with a nominal bore of 20 mm, a wall thickness of 2.8 mm, without thread and without a coupling:

Pipe 20x2.8 GOST 3262-75

The same with the clutch:

Pipe M-20 x 2.8 GOST 3262-75 The same, measured length, threaded:

Pipe R-20x 2.8-4000 GOST 3262-75 The same, with zinc coating, random length, threaded:

Pipe Ts-R-20x 2.8 GOST 3262-75 The same, with zinc coating, measured length, threaded:

Pipe Ts-R-20x 2.8-4000 GOST3262-75

For pipes for thread rolling, the letter H is indicated after the word "pipe" in the symbol.

For pipes with a long thread, the letter D is indicated after the word “pipe” in the symbol. For pipes of increased manufacturing accuracy, the letter P is indicated in the symbol after the size of the nominal bore.

(Revised edition, Rev. No. 1).

2. TECHNICAL REQUIREMENTS

Pipes for parts of water and gas pipeline structures are made of steel according to GOST 1050.

2.2. At the request of the consumer, at the ends of pipes to be welded, with a wall thickness of 5 mm or more, chamfers must be removed at an angle of 35 ° -40 ° to the end of the pipe. In this case, an end ring with a width of 1-3 mm should be left.

At the request of the consumer, on ordinary and reinforced pipes with a nominal bore of more than 10 mm, the thread is applied to both ends of the pipe.

2.1, 2.2. (Changed edition, Rev. No. 3, 4).

2.3. At the request of the consumer, the pipes are equipped with couplings made in accordance with GOST 8944, GOST 8954, GOST 8965 and GOST 8966, at the rate of one coupling for each pipe.

(Revised edition, Rev. No. 3).

2.4. Cracks, captivity, swelling and sunsets are not allowed on the surface of the pipes.

At the ends of the pipes, delamination is not allowed.

On pipes made by furnace welding, it is allowed to reduce the outer diameter to 0.5 mm at the weld site if there is a gentle thickening of the inner diameter of not more than 1.0 mm in this place.

(Changed edition, Rev. No. 3, 4).

(Changed edition, Rev. No. 2, 3, 4, 5, 6).

By agreement between the manufacturer and the consumer, burrs up to 1 mm are allowed on pipes with a nominal bore of 6-25 mm, made by furnace welding.

(Changed edition, Rev. No. 4, 6).

2.7. Galvanized pipes must have a continuous zinc coating over the entire surface with a thickness of at least 30 microns. The absence of zinc coating on the ends and threads of pipes is allowed.

On the surface of galvanized pipes, blistering and foreign inclusions (hardzinc, oxides, sintered charge), peeling of the coating from the base metal are not allowed.

Separate flux spots and traces of pipes being caught by lifting devices, roughness and slight local zinc deposits are allowed.

It is allowed to correct individual non-galvanized sections by 0.5% of the outer surface of the pipe in accordance with GOST 9.307.

(Changed edition, Rev. No. 3, 4).

2.8. Pipes must withstand hydraulic pressure:

2.4 MPa (25 kgf / cm 2) - ordinary and light pipes;

3.1 MPa (32 kgf / cm 2) - reinforced pipes.

At the request of the consumer, the pipes must withstand a hydraulic pressure of 4.9 MPa (50 kgf / cm 2).

At the request of the consumer, the pipes must withstand the expansion test:

for pipes with nominal bore from 15 to 50 mm - not less than 7%;

for pipes with a nominal bore of 65 mm or more - at least 4%.

At the request of the consumer, the pipes must withstand the flattening test up to a distance between flattened surfaces equal to 2/3 of the outer diameter of the pipes.

2.8, 2.9. (Changed edition, Rev. No. 2, 3, 5).

2.10. At the request of the consumer, the mechanical properties of pipes for parts of water and gas pipeline structures must comply with GOST 1050.

2.11. The pipe thread must be clean, without flaws and burrs, and comply with GOST 6357, accuracy class B.

Pipes with cylindrical threads are used when assembling with seals.

2.10, 2.11. (Changed edition, Rev. No. 3, 4).

2.13. It is allowed on the thread to reduce the useful length of the thread (without run-off) up to 15% compared to that indicated in Table. 4, and at the request of the consumer - up to 10%.

2.12, 2.13. (Changed edition, Rev. No. 2, 3, 5).

2.14. Threading on galvanized pipes is carried out after galvanizing.

2.15. (Deleted, Rev. No. 3).

2.16. At the request of the consumer, welded seams of pipes are subjected to control by non-destructive methods.

(Revised edition, Rev. No. 5).

3. ACCEPTANCE RULES

3.1. Pipes are accepted in batches. The batch must consist of pipes of the same size, the same steel grade and be accompanied by one quality document in accordance with GOST 10692 with an addition for pipes intended for the manufacture of parts for water and gas pipeline structures, from steel in accordance with GOST 1050; chemical composition and mechanical properties of steel - in accordance with the document on the quality of the enterprise - the manufacturer of the workpiece.

Party weight - no more than 60 tons.

(Changed edition, Rev. No. 3, 4).

3.2. The surface, dimensions and curvature are checked for each pipe of the batch.

It is allowed to apply statistical control methods according to GOST 18242* with a normal level. Control plans are established by agreement between the manufacturer and the consumer.

The control of the outer diameter of the pipes is carried out at a distance of at least 15 mm from the end of the pipe.

(Changed edition, Rev. No. 3, 4, 5).

(Changed edition, Rev. No. 3, 4).

3.4. All pipes are subjected to weight control.

(Revised edition, Rev. No. 3).

(Revised edition, Rev. No. 6).

3.6. To check the thickness of the zinc coating on the outer surface and in accessible places on the inner surface, two pipes are taken from the lot.

(Revised edition, Rev. No. 2).

3.7. Upon receipt of unsatisfactory test results for at least one of the indicators, it is repeated tests on a double sample.

The retest results apply to the entire lot.

4. TEST METHODS

4.1. For quality control, one sample is cut from each selected pipe for each type of test.

The tensile test is carried out in accordance with GOST 10006. Instead of the tensile test, it is allowed to control the mechanical properties by non-destructive methods.

4.2. Inspection of the surface of the pipes is carried out visually.

4.3. Hydraulic testing is carried out in accordance with GOST 3845 with exposure under test pressure for at least 5 s.

4.4. The bend test is carried out according to GOST 3728. Galvanized pipes are tested before coating.

(Revised edition, Rev. No. 3).

4.4a. The expansion test is carried out according to GOST 8694 on a conical mandrel with a taper angle of 6°.

The test can be carried out on a mandrel with a taper angle of 30°.

(Changed edition, Rev. No. 3, 4).

GOST R 50779.71-99 is valid on the territory of the Russian Federation.

4.46. The flattening test is carried out according to GOST 8695.

(Revised edition, Rev. No. 3).

4.4c. Weld seam control is carried out by non-destructive methods according to normative documentation.

(Introduced additionally, Rev. No. 3).

4.6. The thread is checked with threaded ring gauges according to GOST 2533 (third class of accuracy).

In this case, the screwing of the non-going gauge-ring on the thread should be no more than three turns.

(Changed edition, Rev. No. 3, 4).

4.7. The curvature of the pipes is controlled by a straightedge according to GOST 8026 and a set of probes according to ID.

(Changed edition, Rev. No. 3, 5).

4.8. The right angle of the ends of the pipes is controlled by a 90 ° square with a size of 160 x 100 mm class 3 according to GOST 3749, with lamellar probes of set 4 according to ID or a goniometer according to GOST 5378. The bevel angle of the chamfer is controlled by a goniometer according to GOST 5378.

(Changed edition, Rev. No. 3, 6).

4.9. The control of the outer diameter is carried out with smooth micrometers in accordance with GOST 6507, with staple gauges in accordance with GOST 2216 or GOST 18360.

The length of the pipes is measured with a tape measure in accordance with GOST 7502. The thread is controlled with gauges in accordance with GOST 2533.

The control of the mass of a batch of pipes is carried out on scales not exceeding Utah with a division value of not more than 20 kg.

(Changed edition, Rev. No. 3, 4, 5, 6).

4.10. Weld seam control is carried out by non-destructive methods according to technical documentation.

(Introduced additionally, Rev. No. 4).

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

5.1. Marking, packaging, transportation and storage are carried out in accordance with GOST 10692 with an addition.

5.1.1. Pipe threads must be protected from mechanical damage and corrosion by grease in accordance with regulatory documents.

Sec. 5. (Changed edition, Rev. No. 3).

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Ferrous Metallurgy of the USSR DEVELOPERS

IN AND. Shavings, Ph.D. tech. sciences; V.M. Crow, Ph.D. tech. sciences; Yu.M. Mironov, Ph.D. tech. sciences; A.I. Postolova

2. APPROVED AND INTRODUCED BY Decree of the USSR State Committee for Standards No. 2379 of September 11, 1975

3. Periodicity of inspection - 5 years

4. REPLACE GOST 3262-62

5. REFERENCE REGULATIONS AND TECHNICAL DOCUMENTS

	Item number		Item number
GOST 9.301-86		GOST 7502-98
GOST 9.302-88		GOST 8026-92
GOST 9.307-89		GOST 8694-75
		GOST 8695-75
GOST 1050-88		GOST 8944-75
GOST 2216-84		GOST 8954-75
GOST 2533-88		GOST 8965-75
GOST 3728-78		GOST 8966-75
GOST 3749-77		GOST 10006-80
GOST 3845-75		GOST 10692-80
GOST 5378-88		GOST 11358-89
GOST 6357-81		GOST 18242-72
GOST 6507-90		GOST 18360-93

6. The limitation of the validity period was removed by the Decree of the State Standard of the USSR dated 12.11.91 No. 1726

7. EDITION (May 2007) with Amendments No. 1, 2, 3, 4, 5, 6, approved in November 1977, December 1978, January 1987, May 1988, November 1989 , November 1991 (NUS 1-78, 2-79, 4-87, 8-88, 2-90, 2-92)

Editor L.I. Nakhimova Technical editor O.N. Vlasova Proofreader A.S. Chernousova Computer proofing I.A. Naleykina

Handed over to the set 05/14/2007. Signed for publication on 06/05/2007. Format 60 x 84 Vs - Offset paper. Headset Times. Offset printing. Uel. oven l. 0.93. Uch.-ed. l. 0.80. Circulation 126 copies. Zach. 421. From 4031.

FSUE "STANDARTINFORM", 123995 Moscow, Granatny per., 4. Typed in FSUE "STANDARTINFORM" on a PC

Printed in the branch of FSUE "STANDARTINFORM" - type. "Moscow printer", 105062 Moscow, Lyalin per., 6

home > Agriculture

Welded steel pipes for water and gas pipelines Pipes steel water and gas

1. ASSORTMENT

2. TECHNICAL REQUIREMENTS

3. ACCEPTANCE RULES

4. TEST METHODS

1. ASSORTMENT

Dimensions, mm

2. TECHNICAL REQUIREMENTS

3. ACCEPTANCE RULES

4. TEST METHODS

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

INFORMATION DATA

1. ASSORTMENT

2. TECHNICAL REQUIREMENTS

2.1, 2.2. (Changed edition, Rev. No. 3, 4).

2.8, 2.9. (Changed edition, Rev. No. 2, 3, 5).

2.10, 2.11. (Changed edition, Rev. No. 3, 4).

2.12, 2.13. (Changed edition, Rev. No. 2, 3, 5).

3. ACCEPTANCE RULES

4. TEST METHODS

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

INFORMATION DATA

Classifier OKPD 2

Conventions

File types

GOST statuses

GOST 3262-75 Steel water and gas pipes. Specifications

You can download GOST 3262-75 in the following versions:

Amendments and changes to GOST 3262-75:

INTERSTATE STANDARD

INFORMATION DATA

1. ASSORTMENT

2. TECHNICAL REQUIREMENTS

3. ACCEPTANCE RULES

4. TEST METHODS

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

TECHNICAL CONDITIONS

INTERSTATE

STANDARD

STEEL WATER AND GAS PIPES

Specifications

1. ASSORTMENT

2. TECHNICAL REQUIREMENTS

2.1, 2.2. (Changed edition, Rev. No. 3, 4).

2.8, 2.9. (Changed edition, Rev. No. 2, 3, 5).

2.10, 2.11. (Changed edition, Rev. No. 3, 4).

2.12, 2.13. (Changed edition, Rev. No. 2, 3, 5).

2.15. (Deleted, Rev. No. 3).

3. ACCEPTANCE RULES

4. TEST METHODS

5. MARKING, PACKAGING, TRANSPORT AND STORAGE

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Ministry of Ferrous Metallurgy of the USSR DEVELOPERS

2. APPROVED AND INTRODUCED BY Decree of the USSR State Committee for Standards No. 2379 of September 11, 1975

3. Periodicity of inspection - 5 years

4. REPLACE GOST 3262-62

5. REFERENCE REGULATIONS AND TECHNICAL DOCUMENTS

6. The limitation of the validity period was removed by the Decree of the State Standard of the USSR dated 12.11.91 No. 1726

We also recommend